Mode I Fracture Toughness of Tangential Moso Bamboo

竹藤论文

期刊/会议:

BIORESOURCES

Language:

English

作者:

Xu Minmin; Wu Xiuming; Song Guangnan; Zhang Xiubiao; Zhao Shuangxi

Experts:

Liu Huanrong; Sun Zhengjun

年份:

2014

卷:

9

期:

2

页码:

2026-2032

关键词:

Fracture; COD gauge; Crack opening displacement; Fracture toughness

This paper discusses moso bamboo (Phyllostachys pubescens) with initial crack formation by a three-point bending (SENB) method. The corrected indentation load-displacement curve (ISO 13586-2000) and the crack opening displacement in determining the crack tip extended displacement of the specimen (ASTM E399-09) were measured using a COD gauge. Then, the load-displacement curve and the value of PQ were found by the method of 95% stiffness correction. The results showed that the bamboo has good fracture toughness, and, in this experiment, the fracture results showed little difference; the result for fracture toughness can be up to 17.39 MPa .m(1/2). By observing the crack under the microscope and the failure mode, it was found that the crack propagation was not established in accordance with the crack opening direction; rather it extended along the fiber interface.