Synthesis and 1-butene hydrogenation activity of platinum decorated bamboo-shaped multiwall carbon nanotubes

竹藤论文

期刊/会议:

REACTION KINETICS MECHANISMS AND CATALYSIS

Language:

English

作者:

Vanyorek Laszlo; Kristaly Ferenc; Mihalko Andrea; Banhidi Oliver; Kukovecz Akos; Konya Zoltan; Lakatos Janos

年份:

2015

卷:

116

期:

2

页码:

371-383

关键词:

Bamboo-shaped multiwall carbon nanotubes; Catalyst support; 1-Butene hydrogenation

Bamboo-shaped carbon nanotubes (BCNT) were prepared from three different amines on supported iron (Fe) and nickel (Ni) catalysts by catalytic chemical vapor deposition. The main factors governing product morphology and defect site density were identified. Post-synthetic oxidative functionalization was used to add carboxyl groups to the nanotubes, and then platinum (Pt) nanoparticles were deposited on the surface by the in situ reduction of a platinum salt. The average Pt nanoparticle diameter was found to be affected by the extent of surface functionalization. The catalytic performance of the synthesized Pt/BCNT samples were examined in the hydrogenation of 1-butene, in order to show that the catalytic activity of the bamboo like carbon nanotube supported Pt catalyst is similar to the conventional Pt catalysts in heterogeneous catalytic hydrogenation. The best overall performance was achieved when the bamboo-shaped nanotube support was synthesized on 5 wt% Fe/Al(OH)(3) catalyst from triethylamine and decorated with 5 wt% platinum nanoparticles.